A. Plain NON ASBESTOS RUBBER SHEET
Made from Vegetable Fiber, Kevlar Fiber with beat-fresisting rubber as filler and compressed into sheet form.
TECHNICAL DATA |
WXB200 (GLG303-1) |
WXB300(GLG303-2) |
WXB400(GLG303-3) |
Working Temp. °C |
200 |
300 |
400 |
Tensile Strength Crosswise(MPa) > |
6 |
9 |
12.5 |
Compressibility |
7% ~ 17% |
7% ~ 17% |
7% ~ 17% |
Aging Coefficient>= |
0.9 |
0.9 |
0.9 |
Rebound Degree |
>=40% |
>=45% |
>=45% |
Stress Relaxation % <= |
45 |
45 |
45 |
Flexibility |
NOT BREAK |
NOT BREAK |
NOT BREAK |
STEAM SEALING |
|
|
|
TEMP. °C |
200 |
300 |
400 |
MPa Pressure |
2~3 |
4~5 |
8~9 |
Min No Shock |
30 |
30 |
30 |
B. Oil Resistance NON ASBESTOS RUBBER SHEET
Resistance Made from Vegetable Fiber, Kevlar Fiber with oil-resistance rubber fillers and compressed into sheet
Working Temp. °C |
WNY150(GLG303-4) |
WNY300(GLG303-5) |
WNY350(GLG303-6) |
Tensile Strength Crosswise(MPa) > |
7.0 |
10.0 |
12.0 |
Compressibility |
7% ~ 17% |
7% ~ 17% |
7% ~ 17% |
Aging Coefficient>= |
0.9 |
0.9 |
0.9 |
Rebound Degree |
40 |
40 |
45 |
Stress Relaxation % <= |
45 |
40 |
40 |
Flexibility |
NOT BREAK |
NOT BREAK |
NOT BREAK |
Immersion in 20 |
# aviation |
Lub Oil 5H |
With 150°C |
Tensile Strength Crosswise(MPa) > |
|
6 |
8 |
Oil Absorption |
<=22% |
<=15% |
<=15% |
Thickness Increase % <= |
20 |
10 |
10 |
C. GLG303-7 ACID RESISTANCE NON ASBESTOS RUBBER SHEET
D. GLG303-8 NON ASBESTOS RUBBER SHEET WITH STEEL WIRE REINFORCED
E. GLG303-9 NON ASBESTOS RUBBER SHEET WITH GRAPHITE COATED
|